The precursor sols of Al 2 O 3 and mixed Nb x O y /Al 2 O 3 oxides were synthesized by the sol-gel process using acetylacetone to control the reaction kinetics of the organometallic oxides in the mixture. The layers of the precursor sols of Al 2 O 3 and Nb x O y /Al 2 O 3 were deposited on AISI steel 1020 by manual immersion (dip coating). The lyophilized sols were characterized by X-ray diffraction, thermal analysis and scanning electron microscopy with EDXS before the recoating process. The influence of the ceramic coating of corrosive processes of AISI steel 1020 were investigated by electrochemical measurements. The only identified phase was poorly crystallized boehmite with homogeneous mixture of Al, Nb, O and C ions in mixed Nb x O y /Al 2 O 3 oxides. The ceramic layers deposited appeared to have physical and chemical homogeneity and the steel samples with these deposits had lower corrosion potential. However, the precursor sol Al 2 O 3 showed better steel corrosion protection with lower current density, and more corrosive potential.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.