Abstract. There are more than four decades since the last 1970s where geopolymers concrete was first introduced and developed to use as a replacement to conventional concrete material which uses cement as a binder. And since the last two decades, geopolymers which utilized fly ash as aluminosilicate source material, i.e. fly ash based geopolymers, have been investigated. Many researchers present how to produce the best fly ash based geopolymer with a various source of constituent material as well as mixing formula to achieve exceptional concrete performance. Although there is a similar trend towards factors affecting the result of fly ash based geopolymer synthesis, there is still remain a wide range in mixture proportion. The considerable variation in fly ash characteristics as source material in the synthesis can very likely be one of the causes of this problem. This paper attempts to identify the effect of source material variation of geopolymer concrete, particularly which use fly ash as source material and focuses on the variation of its characteristics and the effects to properties of concrete. From the reviews it concluded that different sources (and even the same source, but different batch) of fly ash materials will give some different characteristics of the fly ash, where it would affect the synthesis process of the fly ash based geopolymer concretes.
Fly ash is a waste from coal burning, that are generated with fluctuation both in its physical and chemical characteristics. This characteristics of fly ash when used in the making of geopolymer concrete will greatly affect the final products obtained. The pH value measured in fly ash, according previous research, can influence the setting time of geopolymer and fly ash with high pH values can cause flash-setting in the concrete. Understanding more clearly about the factors that affect the setting time of fly ash based geopolymer is important for further progress and development of the material. It was found that factors that influence the setting time of geopolymer was not only from the physical and chemical properties of the fly ash itself. Other factors such as composition and mix design, manufacturing process and environmental conditions can also affect its setting time. The experimental results showed that fly ash particle size, CaO and MgO content, in addition to ratio of sodium silicate and sodium hydroxide in the alkali solution, molarity of NaOH, initial temperature of the mixture, curing temperature, and mix volume could potentially influence the setting time of the geopolymer mixture.
Polypropylene composites were prepared from sugarcane bagasse fibers by extrusion and injection molding. Wood flour was used as reference filler in the study. The fiber content of the composites changed between 0 and 30 wt% in 5 wt% steps. Maleated polypropylene was used as coupling agent to improve interfacial adhesion. Mechanical properties were characterized by tensile and fracture testing, while local
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.