No abstract

Biodegradable polymers such as polycaprolactone (PCL) are increasingly used for electrospinning substrates for tissue engineering. These materials offer great advantages such as biocompatibility and good mechanical properties. However, in order to be approved for human implantation they have to be sterilized. The impact of commonly used irradiation sterilization methods on electrospun PCL fiber mats was investigated systematically. Electron beam (β-irradiation), gamma and X-ray irradiation with two different doses (25 and 33 kGy) were investigated. To determine the impact on the fiber mats, mechanical, chemical, thermal properties and crystallinity were investigated. Irradiation resulted in a significant decrease in molecular weight. At the same time, crystallinity of fiber mats increased significantly. However, the mechanical properties did not change significantly upon irradiation, mostly likely because effects of a lower molecular weight were balanced with the higher degree of crystallinity. The irradiation effects were dose dependent, a higher irradiation dose led to stronger changes. Gamma irradiation seemed to be the least suited method, while electron beams (β irradiation) had a lower impact. Therefore, β irradiation is recommended as sterilization method for electrospun PCL fiber mats.

Acute and chronic rotator cuff tears remain challenging for therapy. A wide range of therapeutic approaches were developed but re-tears and postoperative complications occur regularly. Especially in elderly people, the natural regeneration processes are decelerated, and graft materials are often necessary to stabilize the tendon-to-bone attachment and to improve the healing process. We here investigated in a small animal model a newly developed electrospun polycaprolactone fiber implant coated with a chitosan-polycaprolactone graft copolymer and compared these implants biomechanically and histologically with either a commercially available porous polyurethane implant (Biomerix 3D Scaffold) or suture-fixed tendons. Fifty-one rats were divided into three groups of 17 animals each. In the first surgery, the left infraspinatus tendons of all rats were detached, and the animals recovered for 4 weeks. In the second surgery, the tendons were fixed with suture material only (suture-fixed group; n = 17), whereas in the two experimental groups, the tendons were fixed with suture material and the polyurethane implant (Biomerix scaffold group; n = 17) or the modified electrospun polycaprolactone fiber implant (CS-g-PCL scaffold group; n=17), respectively. The unaffected right infraspinatus tendons were used as native controls. After a recovery of 8 weeks, all animals were clinically inconspicuous. In 12 animals of each group, repaired entheses were biomechanically tested for force at failure, stiffness, and modulus of elasticity, and in five animals, repaired entheses were analyzed histologically. Biomechanically, all parameters did not differ statistically significant between both implant groups, and the entheses failed typically at the surgical site.However, with respect to the force at failure, the median values of the two implant groups were smaller than the median value of the suture-fixed group. Histologically, the modified polycaprolactone fiber implant showed no acute inflammation processes, a good infiltration with cells, ingrowth of blood vessels and tendinous tissue, and a normal fibrous ensheathment. Further improvement of the implant material could be achieved by additional implementation of drug delivery systems. Therewith, the used CS-g-PCL fiber mat is a promising basic material to reach the goal of a clinically usable graft for rotator cuff tear repair.Elmar Willbold and Mathias Wellmann contributed equally to this work

Rotator cuff tear is the most frequent tendon injury in the adult population. Despite current improvements in surgical techniques and the development of grafts, failure rates following tendon reconstruction remain high. New therapies, which aim to restore the topology and functionality of the interface between muscle, tendon and bone, are essentially required. One of the key factors for a successful incorporation of tissue engineered constructs is a rapid ingrowth of cells and tissues, which is dependent on a fast vascularization. The dorsal skinfold chamber model in female BALB/cJZtm mice allows the observation of microhemodynamic parameters in repeated measurements in vivo and therefore the description of the vascularization of different implant materials. In order to promote vascularization of implant material, we compared a porous polymer patch (a commercially available porous polyurethane based scaffold from Biomerix™) with electrospun polycaprolactone (PCL) fiber mats and chitosan-graft-PCL coated electrospun PCL (CS-g-PCL) fiber mats in vivo. Using intravital fluorescence microscopy microcirculatory parameters were analyzed repetitively over 14 days. Vascularization was significantly increased in CS-g-PCL fiber mats at day 14 compared to the porous polymer patch and uncoated PCL fiber mats. Furthermore CS-g-PCL fiber mats showed also a reduced activation of immune cells. Clinically, these are important findings as they indicate that the CS-g-PCL improves the formation of vascularized tissue and the ingrowth of cells into electrospun PCL scaffolds. Especially the combination of enhanced vascularization and the reduction in immune cell activation at the later time points of our study points to an improved clinical outcome after rotator cuff tear repair.