Longevity has been a long-standing concern for hybrid perovskite photovoltaics. We demonstrate high-resilience positive-intrinsic-negative perovskite solar cells by incorporating a piperidinium-based ionic compound into the formamidinium-cesium lead-trihalide perovskite absorber. With the bandgap tuned to be well suited for perovskite-on-silicon tandem cells, this piperidinium additive enhances the open-circuit voltage and cell efficiency. This additive also retards compositional segregation into impurity phases and pinhole formation in the perovskite absorber layer during aggressive aging. Under full-spectrum simulated sunlight in ambient atmosphere, our unencapsulated and encapsulated cells retain 80 and 95% of their peak and post-burn-in efficiencies for 1010 and 1200 hours at 60° and 85°C, respectively. Our analysis reveals detailed degradation routes that contribute to the failure of aged cells.
This work reports on a comparative study comprising three transition metal oxides, MoO 3 , WO 3 and V 2 O 5 , acting as front p-type emitters for n-type crystalline silicon heterojunction solar cells. Owing to their high work functions (>5 eV) and wide energy band gaps, these oxides act as transparent hole-selective contacts with semiconductive properties that are determined by oxygen-vacancy defects (MoO 3-x ), as confirmed by x-ray photoelectron spectroscopy. In the fabricated hybrid structures, 15 nm thick transition metal oxide layers were deposited by vacuum thermal evaporation. Of all three devices, the V 2 O 5 /n-silicon heterojunction performed the best with a conversion efficiency of 15.7% and an open-circuit voltage of 606 mV, followed by MoO 3 (13.6%) and WO 3 (12.5%). These results bring into view a new silicon heterojunction solar cell concept with advantages such as the absence of toxic dopant gases and a simplified low-temperature fabrication process.
25.5% efficiency is demonstrated for monolithic perovskite/silicon tandem solar cell using textured foil and the impact of texture position on performance and energy yield is simulated.
Perovskite/silicon tandem solar cells are attractive for their potential for boosting cell efficiency beyond the crystalline silicon (Si) single‐junction limit. However, the relatively large optical refractive index of Si, in comparison to that of transparent conducting oxides and perovskite absorber layers, results in significant reflection losses at the internal junction between the cells in monolithic (two‐terminal) devices. Therefore, light management is crucial to improve photocurrent absorption in the Si bottom cell. Here it is shown that the infrared reflection losses in tandem cells processed on a flat silicon substrate can be significantly reduced by using an optical interlayer consisting of nanocrystalline silicon oxide. It is demonstrated that 110 nm thick interlayers with a refractive index of 2.6 (at 800 nm) result in 1.4 mA cm−² current gain in the silicon bottom cell. Under AM1.5G irradiation, the champion 1 cm2 perovskite/silicon monolithic tandem cell exhibits a top cell + bottom cell total current density of 38.7 mA cm−2 and a certified stabilized power conversion efficiency of 25.2%.
We present a highly efficient monolithic perovskite/silicon tandem solar cell and analyze the tandem performance as a function of photocurrent mismatch with important implications for future device and energy yield optimizations.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.