Polyethylene terephthalate (PET) bottles are widely used as packaging material for natural mineral water. However, trace levels of acetaldehyde can migrate into natural mineral water during the shelf life and might influence the taste of the PET bottled water. 2-Aminobenzamide is widely used during PET bottle production as a scavenging agent for acetaldehyde. The aim of this study was the determination of the migration kinetics of 2-aminobenzamide into natural mineral water as well as into 20% ethanol. From the migration kinetics, the diffusion coefficients of 2-aminobenzamide in PET at 23 and 40°C were determined to be 4.2 × 10− 16 and 4.2 × 10− 15 cm2 s–1, respectively. The diffusion coefficient for 20% ethanol at 40°C was determined to be 7.7 × 10− 15 cm2 s–1, which indicates that 20% ethanol is causing swelling of the PET polymer. From a comparison of migration values between 23 and 40°C, acceleration factors of 9.7 when using water as contact medium and 18.1 for 20% ethanol as simulant can be derived for definition of appropriate accelerated test conditions at 40°C. The European Union regulatory acceleration test based on 80 kJ mol–1 as conservative activation energy overestimates the experimentally determined acceleration rates by a factor of 1.6 and 3.1, respectively.

Materials and articles made of acrylonitrile–butadiene–styrene (ABS) intended for contact with food must comply with the requirements of the European Plastic Regulation (EU) 10/2011, which lays down the food simulants and the time/temperature conditions to be applied for migration testing. Previous studies indicated that high concentrations of ethanol at temperatures above ambient may lead to swelling of ABS polymers resulting in increased migration. In this study migration kinetic data for a set of model substances at different temperatures were obtained using both food simulants stipulated in EU regulations and real food (milk, cream and olive oil). At the same time, the extent of polymer swelling was gravimetrically characterized after contact with simulants and different foods tested at several conditions to cover the majority of foreseeable applications of ABS. The obtained results confirmed that the use of high concentrations of ethanol–water, especially at high temperatures, causes the swelling of ABS polymers and results in significantly higher migration values compared to the tested foods as well as Tenax®. None of the real foods studied cause significant swelling of ABS. The widely used simulant 95% (v/v) aqueous ethanol proves not be suitable for compliance testing of ABS under the recommended conditions of Regulation (EU) 10/2011. Swelling of the polymer results in artificially higher diffusion coefficients or lower activation energies of diffusion. Migration prediction using polymer-specific diffusion parameters should therefore be considered to avoid over-conservative risk assessment for food contact materials and articles made of ABS.

The European Food Safety Authority is re-evaluating styrene for assessing the safety of food contact materials (FCM) such as polystyrene (PS) and started a systematic review of the data on migration levels in food. A restriction for styrene is expected in the near future. The main food contact application of PS is dairy packaging, mainly at refrigerated storage. In this study, seventeen dairy products packed in PS taken from the Italian and German markets were investigated. Styrene concentrations in the refrigerated dairy products (yogurt, cream) ranged from 5 to 30 µg/kg at the best before date, while in single serving portions of coffee creamer, which were stored at room temperature until the best before date of approx. 190 days, 401 µg/kg were measured. Among several parameters, the ratio between the surface contact area of the package and the quantity of the food packed, the time/temperature conditions of production/filling and storage of the products were identified as the main factors influencing styrene migration into food under realistic conditions. Yogurts fermented in the pots for approximately 8 h at 40–50 °C showed higher styrene levels than those fermented in an incubator and filled at 20 °C. The fat content might influence the styrene level but the effect, if any, was too small in relation to the variability of other parameters. Levels of styrene migrating into 50% ethanol food simulant under standardized condition (10 days/40 °C) were found to be much higher than levels in refrigerated foods. This raises the question as to whether compliance testing for PS plastics should be adapted taking into consideration the correlation between migration testing by laboratory simulations and migration into real food.

Migration kinetic data from general purpose polystyrene (GPPS) and high impact polystyrene (HIPS) were generated for a set of model substances as well as styrene monomer and oligomers at different temperatures (20 °C, 40 °C, 60 °C) using food simulants stipulated in the European Regulation (EU) 10/2011 and real foods like milk, cream and olive oil (20 °C, 40 °C). The extent of polymer swelling was characterized gravimetrically and visual changes of the test specimens after migration contact were recorded. Isooctane and 95% ethanol caused strong swelling and visual changes of HIPS, overestimating real migration into foods especially at high temperatures; GPPS was affected by isooctane only at 60 °C. With 50% ethanol, after 10 days contact at 60 °C or 40 °C both polymers were slightly swollen. Contrary, most of the real foods analyzed caused no detectable swelling or visual changes of the investigated polymers. This study demonstrates that the recommendations provided by EU regulations are not always in agreement with the physicochemical properties of styrenic polymers. The critical point remains the selection of adequate food simulants/testing conditions, since the high overestimation of aggressive media can lead to non-compliance of polystyrene materials even if the migration into real food would be of no concern.

No abstract