An array of magic-angle spinning (MAS) nuclear magnetic resonance (NMR) spectroscopy experiments is applied to explore the surface reactions of a mesoporous bioactive glass (MBG) of composition Ca0.10Si0.85P0.04O1.90 when subjected to a simulated body fluid (SBF) for variable intervals. Powder X-ray diffraction and 31P NMR techniques are employed to quantitatively monitor the formation of an initially amorphous calcium phosphate surface layer and its subsequent crystallization into hydroxycarbonate apatite (HCA). Prior to the onset of HCA formation, 1H → 29Si cross-polarization (CP) NMR evidence dissolution of calcium ions; a slightly increased connectivity of the speciation of silicate ions is observed at the MBG surface over 1 week of SBF exposure. The incorporation of carbonate and sodium ions into the bioactive orthophosphate surface layer is explored by 1H → 13C CPMAS and 23Na NMR, respectively. We discuss similarities and distinctions in composition−bioactivity relationships established for traditional melt-prepared bioglasses compared to MBGs. The high bioactivity of phosphorus-bearing MBGs is rationalized to stem from an acceleration of their surface reactions due to presence of amorphous calcium orthophosphate clusters of the MBG pore wall.
We report novel symmetry-based pulse sequences for exciting double-quantum (2Q) coherences between the central transitions of half-integer spin quadrupolar nuclei in the NMR of rotating solids. Compared to previous 2Q-recoupling techniques, numerical simulations and 23Na and 27Al NMR experiments on Na2SO4 and the open-framework aluminophosphate AlPO-CJ19 verify that the new dipolar recoupling schemes display higher robustness to both radio-frequency field inhomogeneity and to spreads in resonance frequencies. These advances allowed for the first demonstration of 2Q-recoupling in an amorphous solid for revealing its intermediate-range structural features, in the context of mapping 27Al-27Al connectivities between the aluminium polyhedra (AlO4, AlO5 and AlO6) of a lanthanum aluminate glass (La0.18Al0.82O1.5).
We review the benefits of using 29Si and 1H magic angle spinning (MAS) nuclear magnetic resonance (NMR) spectroscopy for probing the local structures of both bulk and surface portions of mesoporous bioactive glasses (MBGs) of the CaO–SiO2−(P2O5) system. These mesoporous materials exhibit an ordered pore arrangement, and are promising candidates for improved bone and tooth implants. We discuss experimental MAS NMR results from three MBGs displaying different Ca, Si and P contents: the 29Si NMR spectra were recorded either directly by employing radio-frequency pulses to 29Si, or by magnetization transfers from neighbouring protons using cross polarization, thereby providing quantitative information about the silicate speciation present in the pore wall and at the MBG surface, respectively. The surface modifications were monitored for the three MBGs during their immersion in a simulated body fluid (SBF) for intervals between 30 min and one week. The results were formulated as a reaction sequence describing the interconversions between the distinct silicate species. We generally observed a depletion of Ca2+ ions at the MBG surface, and a minor condensation of the silicate-surface network over one week of SBF soaking.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.