We demonstrate that rigidifying the structure of fluorescent linkers by structurally constraining them in metal-organic frameworks (MOFs) to control their conformation effectively tunes the fluorescence energy and enhances the quantum yield. Thus, a new tetraphenylethylene-based zirconium MOF exhibits a deep-blue fluorescent emission at 470 nm with a unity quantum yield (99.9 ± 0.5%) under Ar, representing ca. 3600 cm(-1) blue shift and doubled radiative decay efficiency vs the linker precursor. An anomalous increase in the fluorescence lifetime and relative intensity takes place upon heating the solid MOF from cryogenic to ambient temperatures. The origin of these unusual photoluminescence properties is attributed to twisted linker conformation, intramolecular hindrance, and framework rigidity.
A metal-organic framework (MOF) for reversible alteration of guest molecule adsorption, here carbon dioxide, upon photochemical or thermal treatment has been discovered. An azobenzene functional group, which can switch its conformation upon light irradiation or heat treatment, has been introduced to the organic linker of a MOF. The resulting MOF adsorbs different amount of CO(2) after UV or heat treatment. This remarkable stimuli-responsive adsorption effect has been demonstrated through experiments.
Redox-active organic materials have gained growing attention as electrodes of rechargeable batteries. However, their key limitations are the low electronic conductivity and limited chemical and structural stability under redox conditions. Herein, we report a new cobalt-based 2D conductive metal-organic framework (MOF), Co-HAB, having stable, accessible, dense active sites for high-power energy storage device through conjugative coordination between a redox-active linker, hexaaminobenzene (HAB), and a Co(II) center. Given the exceptional capability of Co-HAB for stabilizing reactive HAB, a reversible three-electron redox reaction per HAB was successfully demonstrated for the first time, thereby presenting a promising new electrode material for sodium-ion storage. Specifically, through synthetic tunability of Co-HAB, the bulk electrical conductivity of 1.57 S cm was achieved, enabling an extremely high rate capability, delivering 214 mAh g within 7 min or 152 mAh g in 45 s. Meanwhile, an almost linear increase of the areal capacity upon increasing active mass loading up to 9.6 mg cm was obtained, demonstrating 2.6 mAh cm with a trace amount of conducting agent.
Conductive metal-organic frameworks (c-MOFs) have shown outstanding performance in energy storage and electrocatalysis. Varying the bridging metal species and the coordinating atom are versatile approaches to tune their intrinsic electronic properties in c-MOFs. Herein we report the first synthesis of the oxygen analog of M(CX) (X = NH, S) family using Cu(II) and hexahydroxybenzene (HHB), namely Cu-HHB [Cu(CO)], through a kinetically controlled approach with a competing coordination reagent. We also successfully demonstrate an economical synthetic approach using tetrahydroxyquinone as the starting material. Cu-HHB was found to have a partially eclipsed packing between adjacent 2D layers and a bandgap of approximately 1 eV. The addition of Cu-HHB to the family of synthetically realized M(CX) c-MOFs will enable greater understanding of the influence of the organic linkers and metals, and further broadens the range of applications for these materials.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.