Kapton polyimde is extensively used in solar arrays, spacecraft thermal blankets, and space inflatable structures. Upon exposure to atomic oxygen in low Earth orbit (LEO), Kapton is severely eroded. An effective approach to prevent this erosion is to incorporate polyhedral oligomeric silsesquioxane (POSS) into the polyimide matrix by copolymerizing POSS monomers with the polyimide precursor. The copolymerization of POSS provides Si and O in the polymer matrix on the nano level. During exposure of POSS polyimide to atomic oxygen, organic material is degraded, and a silica passivation layer is formed. This silica layer protects the underlying polymer from further degradation. Laboratory and space-flight experiments have shown that POSS polyimides are highly resistant to atomic-oxygen attack, with erosion yields that may be as little as 1% those of Kapton. The results of all the studies indicate that POSS polyimide would be a space-survivable replacement for Kapton on spacecraft that operate in the LEO environment.
Two cyanate ester resins and a polycarbonate thermoplastic have been synthesized from vanillin. The bisphenol precursors were prepared by both an electrochemical route as well as by a McMurry coupling reaction. 1,2-bis(4-cyanato-3-methoxyphenyl)ethene (6) had a high melting point of 237 °C and did not cure completely under a standard cure protocol. In contrast, the reduced version, 1,2-bis(4-cyanato-3-methoxyphenyl)ethane (7) melted at 190 °C and underwent complete cure to form a thermoset material with T g = 202 °C. 7 showed thermal stability up to 335 °C and decomposed via formation of phenolics and isocyanic acid. A polycarbonate was then synthesized from the reduced bisphenol by a transesterification reaction with diphenylcarbonate. The polymer had M n = 3588, M w /M n = 1.9, and a T g of 86 °C. TGA/FTIR data suggested that the polycarbonate decomposed via formation of benzodioxolanes with concomitant elimination of methane. The results show that vanillin is a useful precursor to both thermosetting resins and thermoplastics without significant modification.
A series of renewable bis(cyanate) esters have been prepared from bisphenols synthesized by condensation of 2-methoxy-4-methylphenol (creosol) with formaldehyde, acetaldehyde, and propionaldehyde. The cyanate esters have been fully characterized by infrared spectroscopy, (1)H and (13)C NMR spectroscopy, and single crystal X-ray diffraction. These compounds melt from 88 to 143 °C, while cured resins have glass transition temperatures from 219 to 248 °C, water uptake (96 h, 85 °C immersion) in the range of 2.05-3.21%, and wet glass transition temperatures from 174 to 193 °C. These properties suggest that creosol-derived cyanate esters may be useful for a wide variety of military and commercial applications. The cure chemistry of the cyanate esters has been studied with FTIR spectroscopy and differential scanning calorimetry. The results show that cyanate esters with more sterically demanding bridging groups cure more slowly, but also more completely than those with a bridging methylene group. In addition to the structural differences, the purity of the cyanate esters has a significant effect on both the cure chemistry and final Tg of the materials. In some cases, post-cure of the resins at 350 °C resulted in significant decomposition and off-gassing, but cure protocols that terminated at 250-300 °C generated void-free resin pucks without degradation. Thermogravimetric analysis revealed that cured resins were stable up to 400 °C and then rapidly degraded. TGA/FTIR and mass spectrometry results showed that the resins decomposed to phenols, isocyanic acid, and secondary decomposition products, including CO2. Char yields of cured resins under N2 ranged from 27 to 35%, while char yields in air ranged from 8 to 11%. These data suggest that resins of this type may potentially be recycled to parent phenols, creosol, and other alkylated creosols by pyrolysis in the presence of excess water vapor. The ability to synthesize these high temperature resins from a phenol (creosol) that can be derived from lignin, coupled with the potential to recycle the composites, provides a possible route to the production of sustainable, high-performance, thermosetting resins with reduced environmental impact.
Renewable phenols derived from biomass sources often contain methoxy groups that alter the properties of derivative polymers. To evaluate the impact of o-methoxy groups on the performance characteristics of cyanate ester resins, three bisphenols derived from the renewable phenol creosol were deoxygenated by conversion to ditriflates followed by palladium-catalyzed elimination and hydrolysis of the methoxy groups. The deoxygenated bisphenols were then converted to the following cyanate ester resins: bis(4-cyanato-2-methylphenyl)methane (16), 4,4′-(ethane-1,1′-diyl)bis(1-cyanato-3-methylbenzene) (17), and 4,4′-(propane-1,1′-diyl)bis-(1-cyanato-3-methylbenzene) (18). The physical properties, cure chemistry, and thermal stability of these resins were evaluated and compared to those of cyanate esters derived from the oxygenated bisphenols. 16 and 18 had melting points 37 and >95°C lower, respectively, than the oxygenated versions, while 17 had a melting point 14°C higher. The T g 's of thermosets generated from the deoxygenated resins ranged from 267 to 283°C, up to 30°C higher than the oxygenated resins, while the onset of thermal degradation was 50−80°C higher. The deoxygenated resins also exhibited water uptakes up to 43% lower and wet T g s up to 37°C higher than the oxygenated resins. TGA-FTIR of thermoset networks derived from 16−18 revealed a different decomposition mechanism compared to the oxygenated resins. Instead of a low-temperature pathway that resulted in the evolution of phenolic compounds, 16−18 had significantly higher char yields and decomposed via evolution of small molecules including isocyanic acid, CH 4 , CO 2 , and NH 3 .
A renewable bisphenol, 4,4'-(butane-1,4-diyl)bis(2-methoxyphenol), was synthesized on a preparative scale by a solvent-free, Ru-catalyzed olefin metathesis coupling reaction of eugenol followed by hydrogenation. After purification, the bisphenol was converted to a new bis(cyanate) ester by standard techniques. The bisphenol and cyanate ester were characterized rigorously by NMR spectroscopy and single-crystal X-ray diffraction studies. After complete cure, the cyanate ester exhibited thermal stability in excess of 350 °C and a glass transition temperature (Tg ) of 186 °C. As a result of the four-carbon chain between the aromatic rings, the thermoset displayed a water uptake of only 1.8% after a four day immersion in 85 °C water. The wet Tg of the material (167 °C) was only 19 °C lower than the dry Tg , and the material showed no significant degradation as a result of the water treatment. These results suggest that this resin is well suited for maritime environments and provide further evidence that full-performance resins can be generated from sustainable feedstocks.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.