Structural and magnetic properties of Fe oxide nanoparticles prepared by laser pyrolysis and annealed in high pressure hydrogen atmosphere were investigated. The annealing treatments were performed at 200 °C (sample A200C) and 300 °C (sample A300C). The as prepared sample, A, consists of nanoparticles with ~ 4 nm mean particle size and contains C (~ 11 at.%), Fe and O. The Fe/O ratio is between γ-Fe2O3 and Fe3O4 stoichiometric ratios. A change in the oxidation state, crystallinity and particle size is evidenced for the nanoparticles in sample A200C. The Fe oxide nanoparticles are completely reduced in sample A300C to α-Fe single phase. The blocking temperature increases from 106 K in A to 110 K in A200C and above room temperature in A300C, where strong inter-particle interactions are evidenced. Magnetic parameters, of interest for applications, have been considerably varied by the specific hydrogenation treatments, in direct connection to the induced specific changes of particle size, crystallinity and phase composition. For the A and A200C samples, a field cooling dependent unidirectional anisotropy was observed especially at low temperatures, supporting the presence of nanoparticles with core–shell-like structures. Surprisingly high MS values, almost 50% higher than for bulk metallic Fe, were evidenced in sample A300C.
An original photodetector system based on self-connected CuO–ZnO radial core–shell heterojunction nanowire arrays grown on metallic interdigitated electrodes, operating as visible-light photodetector was developed by combining simple preparation approaches. Metallic interdigitated electrodes were fabricated on Si/SiO2 substrates using a conventional photolithography process. Subsequently, a Cu layer was electrodeposited on top of the metallic interdigitated electrodes. The CuO nanowire arrays (core) were obtained by thermal oxidation in air of the Cu layer. Afterwards, a ZnO thin film (shell) was deposited by RF magnetron sputtering covering the surface of the CuO nanowires. The morphological, structural, compositional, optical, electrical and photoelectrical properties of the CuO nanowire arrays and CuO–ZnO core–shell nanowire arrays grown on metallic interdigitated electrodes were investigated. The performances of the devices were evaluated by assessing the figures of merit of the photodetectors based on self-connected CuO–ZnO core–shell heterojunction nanowire arrays grown on the metallic interdigitated electrodes. The radial p–n heterojunction formed between CuO and ZnO generates a type II band alignment that favors an efficient charge separation of photogenerated electron–hole pairs at the CuO–ZnO interface, suppressing their recombination and consequently enhancing the photoresponse and the photoresponsivity of the photodetectors. The electrical connections in the fabricated photodetector devices are made without any additional complex and time-consuming lithographic step through a self-connecting approach for CuO–ZnO core–shell heterojunction nanowire arrays grown directly onto the Ti/Pt metallic interdigitated electrodes. Therefore, the present study provides an accessible path for employing low dimensional complex structures in functional optoelectronic devices such as photodetectors.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.