One of the most studied deleterious phases in stainless steels is the sigma phase, due to its high potential to decrease the toughness and corrosion resistance of these steels. Eight samples of as-received cold rolled UNS S32205 duplex stainless steel were submitted to isothermal heat treatments at 850 o C during 10,15, 30, 60, 120, 180, 240, and 300 minutes in order to study the precipitation kinetics of the sigma and chi deleterious phases. Several complementary microstructural analysis techniques were used to determine the volume fraction of the intermetallic phases, including optical microscopy and scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDS). Evaluation was made of the kinetics of isothermal formation of sigma and chi phases in commercial duplex stainless steels (UNS S32205). The results indicated two different mechanisms for sigma phase precipitation: sigma phase formed from the chi phase for shorter isothermal heat treatment times, and sigma phase precipitated at the ferrite-austenite interface for longer isothermal heat treatment times, using a temperature of 850 o C. The phase transformation kinetics determined using the JMA equation indicated that chi phase precipitation caused faster sigma phase formation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.