Electrochromism was studied with Nb20~ layers prepared by thermal oxidation of niobium. The Nb~O~ layers are crystalline and the morphology and thickness of these films play an important role in the response of electrochromic process. Cyclic voltammetry and chronopotentiometry were carried out together with ellipsometric measurements in electrochromic region. ESCA spectra of the electroreduced oxide suggest that Nb(V) is reduced to a lower valence state such as Nb(IV), and a chemical bond is formed between H § inserted into the oxide and O-2 of the oxide. For Nb205 films the coloration is due to a simultaneous injection of electrons and H § ions.
The aim of this study was to evaluate the effects of simulated pulpal pressure (SPP) on the variation of intrapulpal temperature (ΔT) and microtensile bond strength (μTBS) to dentin submitted to an adhesive technique using laser irradiation. One hundred sound human molars were randomly divided into two groups (n = 50), according to the presence or absence of SPP (15 cm H2O). Each group was divided into five subgroups (n = 10) according to Nd:YAG laser energy (60, 80, 100, 120, 140 mJ/pulse). The samples were sequentially treated with the following: 37 % phosphoric acid, adhesive (Scotchbond Universal), irradiation with Nd:YAG laser (60 s), and light curing (10 s). ΔT was evaluated during laser irradiation using a type K thermocouple. Next, a composite resin block was build up onto the irradiated area. After 48 h, samples were submitted to microtensile test (10 kgf load cell, 0.5 mm/min). Data were analyzed by two-way ANOVA and Tukey tests (p = 0.05). ANOVA revealed significant differences for ΔT and TBS in the presence of SPP. For ΔT, the highest mean (14.3 ± 3.23 °C)(A) was observed in 140 mJ and without SPP. For μTBS, the highest mean (33.4 ± 4.15 MPa)(A) was observed in 140 mJ and without SPP. SPP significantly reduced both ΔT and μTBS during adhesive procedures, lower laser energy parameters resulted in smaller ΔT, and the laser parameters did not influence the μTBS values.
The poly(furfuryl alcohol) is highly indicated to obtain advanced carbonaceous materials due mainly to its good carbon yield (around 50%) and a controllable cure reaction. In the processing of some carbonaceous materials, such as monolithic vitreous carbon, it is necessary to make sure that the material has the smallest porosity to be used in nobler applications such as heart valves and aerospace integrated systems. In this manuscript, a design of experiments was used to study the influence of viscosity, pH, and moisture in the porosity of the cured material. This study shows that the moisture exerts a significant influence on the porosity and the trend of the results lead to conclude that lower viscosity and moisture, and the use of non-neutralized poly(furfuryl alcohol) resins lead to obtain materials with better quality.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.