Objective: To evaluate the effects of surface treatment and repair material on the repair shear bond strength (SBS) of the bioactive restorative material. Methods: A total of 240 Activa BioActive Restorative (Activa) discs were prepared, aged, and polished, and divided randomly into eight groups ( n = 30). Groups 1–4 discs were repaired with bulk-fill flowable resin-based composite (Bulk-RBC), and Groups 5–8 discs with Activa. Surface treatment used for each repair material type were air abrasion with silica-coated 30-m Al2O3 particles (air abrasion) (Groups 2 & 6), Air abrasion with universal primer (Groups 3 & 7), and Air abrasion with universal adhesive (Groups 4 & 8). Groups 1 and 5 were controls without surface treatment. SBS test was performed, and the failure mode and surface topography were assessed. Results: Surface treatment with air abrasion significantly improved the SBS for repair using both Activa and Bulk-RBC. Repair SBS using Activa was significantly higher compared with Bulk-RBC. Cohesive failure in substrate and mixed failures were most common in the surface-treated groups (2–4, 6–8). Air abrasion produced prominent surface topography changes compared with polishing. Conclusion: Air abrasion enhances the repair SBS of aged bioactive restorative material. The use of the same material (Activa) for repair affords a higher bond strength compared with the use bulk-RBC.
Conventional osteotomy techniques can, in some cases, induce higher stress on bone during implant insertion as a result of higher torque. The aim of the present study was to evaluate and compare the stress exerted on the underlying osseous tissues during the insertion of a tapered implant using different osteotomy techniques through a dynamic finite element analysis which has been widely applied to study biomedical problems through computer-aided software. In three different types of osteotomy techniques, namely conventional (B1), bone tap (B2), and countersink (B3), five models and implants designed per technique were prepared, implant insertion was simulated, and stress exerted by the implant during each was evaluated. Comparison of stress scores on the cortical and cancellous bone at different time points and time intervals from initiation of insertion to the final placement of the implant was made. There was a highly statistically significant difference between B1 and B2 (p = 0.0001) and B2 and B3 (p = 0.0001) groups. In contrast, there was no statistically significant difference in the stress scores between B1 and B3 (p = 0.3080) groups at all time points of implant placement. Overall, a highly significant difference was observed between the stresses exerted in each technique. Within the limitations of our study, bone tap significantly exerted lesser stresses on the entire bone than conventional and countersink type of osteotomy procedures. Considering the stress distribution at the crestal region, the countersink showed lower values in comparison to others.
Background: Silane-containing universal adhesives (UAs) are marketed as adhesion promotors for glass-ceramics. Objectives: This study aimed to evaluate the priming capacity of γ-methacryloxypropyltrimethoxysilane (γMPTS)-containing and γ-methacryloxypropyltriethoxysilane (γMPTES)/3-(aminopropyl)triethoxysilane (APTES)-containing universal adhesives (UAs) for lithium disilicate ceramic (LDC). Materials and Methods: Etched LDC discs were distributed into four groups according to the priming material used: (control), no priming; (MBN), LDC was primed with a universal primer (Monobond N); (SBU), γMPTS-containing UA (Single Bond Universal Adhesive) was used as a primer; and (SBP), γMPTES/APTES-containing UA (Scotchbond Universal Plus Adhesive) was used as a primer. LDC discs were cemented using a dual-cure resin cement, then sectioned into microbeams for microtensile bond strength (μTBS) evaluation. Failure modes were assessed. Results: MBN application showed the highest μTBS among all groups. γMPTES/APTES-containing UA (SBP) resulted in considerably higher μTBS compared with γMPTS-containing UA (SBU) or the control group. The mixed failures were the most predominant among all groups. Conclusions: The effect of silane-containing UAs on resin-ceramic μTBS is material dependent. Although γMPTES/APTES-containing UA improved bonding to LDC, the priming of LDC with either of the UAs tested cannot be considered as an alternative to a separate silanization (priming) step using a universal primer.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.