Much effort has been made to enhance the toughness of poly (lactic acid) (PLA) to broaden its possible range of usage in technical applications. In this work, the compatibility of PLA with a partly bio-based ethylene-propylene-diene-rubber (EPDM) through reactive extrusion was investigated. The concentration of EPDM in the PLA matrix was in the range of up to 20%. The reactive extrusion was carried out in a conventional twin-screw extruder. Contact angle measurements were performed to calculate the interfacial tension and thus the compatibility between the phases. The thermal and mechanical properties as well as the phase morphology of the blends were characterized. A copolymer of poly (ethylene-co-methyl acrylate-co-glycidyl methacrylate) (EMAGMA) was used as compatibilizer, which leads to a significant reduction in the particle size of the dispersed rubber phase when compared with the blends without this copolymer. The use of EMAGMA combined with soybean oil (SBO) and a radical initiator enhances the elongation at break of the compound. The results indicate that the reduction of the particle size of the dispersed phase obtained with the compatibilizer alone is not sufficient to improve the mechanical properties of the blend system. The induced radical reactions also influenced the mechanical properties of the blend significantly.
One possible way to increase the use of bioplastics and thus contribute to a more resource-efficient and sustainable economy is to broaden the application range of such bioplastics. Poly(lactic acid) (PLA) is a promising and commercially available bio-based and biologically degradable polymer, which exhibits a high strength and stiffness but is very brittle. Blending with other polymers can lead to an enhancement of the ductility of the PLA. The goal of this work was to show that blending of PLA with a bio-based thermoplastic polyester-urethane elastomer (TPU) increases the ductility of the compound and also affects the adhesion of the layers when the materials – the modified PLA compound and the TPU – are processed via two-component (2C) injection molding to form corresponding composite parts. The results show that both goals – the increased ductility as well as the increased adhesion between the polymeric phases in 2C parts – can be reached by compounding PLA with two different bio-based polyester-based TPUs. Tensile strength and Young’s modulus of the compounds decrease according to a linear mixing rule with the addition of TPU. Elongation at break and notched Charpy impact strength increase by 750 and 200%, respectively. By addition of the TPU, the surface free energies of the compounds were increased, especially the polar parts. This led to reduced interfacial tensions between the produced compounds and the neat TPUs and thus increased the adhesion between them. For the softer TPU the adhesion was so strong that the TPU showed a cohesive failure in the 90° peel test and thus could not be separated from the compound substrate at all. For the harder TPU the bonding strength increased by 140% upon the addition of this TPU inside the hard component.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.