In this paper, we report on the synthesis—via the wet chemical precipitation route method—and thin film characteristics of inorganic semiconductor, cuprous oxide (Cu2O) nanoparticles, for their potential application in enhancing the humidity-sensing properties of semiconducting polymer poly(9,9-dioctylfluorene) (F8). For morphological analysis of the synthesized Cu2O nanoparticles, transmission electron microscope (TEM) and scanning electron microscope (SEM) micrographs are studied to investigate the texture, distribution, shape, and sizes of Cu2O crystallites. The TEM image of the Cu2O nanoparticles exhibits somewhat non-uniform distribution with almost uniform shape and size having an average particle size of ≈24 ± 2 nm. Fourier transformed infrared (FTIR) and X-ray diffraction (XRD) spectra are studied to validate the formation of Cu2O nanoparticles. Additionally, atomic force microscopy (AFM) is performed to analyze the surface morphology of polymer-inorganic (F8-Cu2O) nanocomposites thin film to see the grain sizes, mosaics, and average surface roughness. In order to study the enhancement in sensing properties of F8, a hybrid organic–inorganic (F8-Cu2O) surface-type humidity sensor Ag/F8-Cu2O/Ag is fabricated by employing F8 polymer as an active matrix layer and Cu2O nanoparticles as a dopant. The Ag/F8-Cu2O/Ag device is prepared by spin coating a 10:1 wt% solution of F8-Cu2O nanocomposite on pre-patterned silver (Ag) electrodes on glass. The inter-electrode gap (≈5 μm) between Ag is developed by photolithography. To study humidity sensing, the Ag/F8-Cu2O/Ag device is characterized by measuring its capacitance (C) as a function of relative humidity (%RH) at two different frequencies (120 Hz and 1 kHz). The device exhibits a broad humidity sensing range (27–86%RH) with shorter response time and recovery time, i.e., 9 s and 8 s, respectively. The present results show significant enhancement in the humidity-sensing properties as compared to our previously reported results of Ag/F8/Ag sensor wherein the humidity sensing range was 45–78%RH with 15 s and 7 s response and recovery times, respectively. The improvement in the humidity-sensing properties is attributed to the potential use of Cu2O nanoparticles, which change the hydrophobicity, surface to volume ratio of Cu2O nanoparticles, as well as modification in electron polarizability and polarity of the F8 matrix layer.
This paper reports on the fabrication and photovoltaic characteristics of a heterojunction solar cell based on an organic small molecular semiconductor, N-749 black dye (N749-BD). To investigate the photovoltaic characteristics of N749-BD, an ITO/PEDOT:PSS/N749-BD/Ag device is prepared by spin casting a 100 ± 5-nm thin film of N749-BD on the poly(3,4, ethylene dioxythiophene):polystyrene sulfonate (PEDOT:PSS) film, which acts as buffer/hole transport layer (HTL) and indium tin oxide (ITO) is employed as a transparent conducting substrate. Under standard testing conditions (STC), i.e., 25 °C, 1.5 AM global and 100 mW/cm2 irradiation, the photovoltaic parameters of the device, such as fill factor (FF) and power conversion efficiency (PCE), are found to be 0.65 and 3.8% ± 0.5%, respectively. Current-voltage (I–V) characteristics of the device are also studied in dark conditions to measure reverse saturation current (I0), series resistance at the interface, rectification ratio (RR), barrier height (ϕb) and ideality factor (n). Optical bandgaps (Eg) of N749-BD thin film are found by applying Tauc’s plot on its ultraviolet-visible (UV-Vis) spectrum, which are measured to be 1.68, 2.67, 3.52 and 4.16 eV. External quantum efficiency (EQE) measurements of the fabricated device are studied, which demonstrate large value of EQE ≈ 12.89%, with peak intensity at 626 nm. Bond dynamics and compositional analysis of N749-BD is carried out via Fourier transformed infrared (FTIR) spectroscopy. Morphology of the thin film of N749-BD on quartz glass are investigated via scanning electron microscopy (SEM) with in-situ energy dispersive X-ray (EDX) spectroscopy which exhibits random distribution of N749-BD grains across the surface with nearly uniform grain sizes and shapes. The larger values of FF, PCE and EQE of ITO/PEDOT:PSS/N749-BD/Ag device suggests the potential of N749-BD to be utilized in low cost, simple manufacturing process and high performance of solar cells.
This work reports on the synthesis of small molecular semiconductor 2-(1H-pyrrol-1-yl)-anthracene-9,10-dione (PAD) via wet chemical precipitation route method for its possible potential applications in sensors. Thin film characterization of the synthesized PAD is carried out by studying its surface morphology, bond dynamics, and optical properties. For studying sensing characteristics of the PAD, its 100 nm thick film is thermally deposited on pre-patterned silver (Ag) electrodes over glass substrate having ~45 µm inter-electrode gaps to prepare Ag/PAD/Ag sensor. The effects of humidity (%RH), temperature (T), and illumination of light (Ev) on the fabricated Ag/PAD/Ag sensor are studied by changing one of the three (%RH, T, and Ev) parameters at a time and measuring the corresponding variations in capacitance (C) and capacitive reactance (X) of the device. As C and X also depend on frequency, sensing properties of the Ag/PAD/Ag sensor are measured at two different frequencies (120 Hz and 1 kHz) to find the optimum sensitivity conditions. To investigate reproducibility and repeatability of Ag/PAD/Ag sensor, each measurement is taken several times and also hysteresis loops of %RH vs. C are plotted at 120 Hz and 1 kHz to find the percent errors in each cycle of measurements. The sensor is active to sense humidity, temperature, and illumination within a broad range, i.e., from 15–93%RH, 293–382 K, and 1500–20,000 lx, respectively. Other key parameters of the sensor i.e., the humidity response time (TRes) and recovery time (TRec), are measured, which are 5 and 7 s, respectively, whereas for light sensing the values of TRes and TRec are measured to be 3.8 and 2.6 s, respectively. The measured values of TRes and TRec for the fabricated Ag/PAD/Ag sensor are shorter and better as compared to those of previously reported for similar kind of small molecular based sensors. The sensing properties of Ag/PAD/Ag device exhibit the potential of PAD for humidity, temperature, and light sensing applications.
The appropriate combination of semiconducting polymer–inorganic nanocomposites can enhance the existing performance of polymers-only-based photovoltaic devices. Hence, polyaniline (PANI)/zinc oxide (ZnO) nanocomposites were prepared by combining ZnO nanoparticles with PANI in four distinct ratios to optimize their photovoltaic performance. Using a simple coating method, PANI, ZnO, and its nanocomposite, with varying weight percent (wt%) concentrations of ZnO nanoparticles, i.e., (1 wt%, 2 wt%, 3 wt%, and 4 wt%), were fabricated and utilized as an active layer to evaluate the potential for the high-power conversion efficiency of various concentrations, respectively. PANI/ZnO nanocomposites are characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), atomic force microscopy (AFM), Fourier transform infrared (FTIR) spectroscopy, ultraviolet-visible (UV-vis) absorption, energy dispersive X-ray (EDX), and I-V measurement techniques. The XRD analysis showed a distinct, narrow peak, which corresponds to the wurtzite ZnO (101) plane. The SEM analysis verified the production of the PANI/ZnO composite by demonstrating that the crystalline ZnO was integrated into the PANI matrix. The elemental composition was determined by energy dispersive X-ray analysis (EDX), which confirmed the existence of PANI and ZnO without any impurities, respectively. Using Fourier transform infrared (FTIR) spectroscopy, various chemical bonds and stretching vibrations were analyzed and assigned to different peaks. The bandgap narrowing with an increasing PANI/ZnO composition led to exceptional optical improvement. The I-V characterization was utilized to investigate the impact of the nanocomposite on the electrical properties of the PANI/ZnO, and various concentrations of ZnO (1 wt%, 2 wt%, 3 wt%, and 4 wt%) in the PANI matrix were analyzed under both light and dark conditions at an STC of 1.5 AM globally. A high PCE of 4.48% was achieved for the PANI/ZnO (3 wt%), which revealed that the conductivity of the PANI/ZnO nanocomposite thin films improved with the increasing nanocomposite concentration.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.