Pristine and Cu-doped ZnO thins films were deposited on Si(100) and quartz substrates by the sol–gel method, followed by post annealing at 450 °C. Structural analysis shows that all grown films are polycrystalline in nature and the crystallite size of the doped film increases with the doping concentration. Narrowing of the band gap is seen with Cu doping, and electrical analysis shows an increase in the conductivity and carrier concentration with Cu doping. As compared to pristine ZnO, Cu-doped thin films show p-type conductivity with a maximum carrier concentration of 1.34 × 10 15 cm –3 for 6% doping at room temperature. The p-type conductivity in these films easily degraded with time, which may be due to the interaction of films with ambient conditions or may be due to the diffusion of indium inside the material. After 15 days, ambient-exposed films were totally converted into n-type, whereas the vacuum-placed film still shows p-type behavior with good mobility. This study shows that sol–gel-derived Cu-doped thin films show low electrical resistivity, p-type conductivity, and high transmittance and can be used for optoelectronics devices if these films were well prepared, protected, and properly passivated.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.