Two extreme compositions of the manganese-cobalt oxide system Mn x Co 3-x O 4 namely Co 3 O 4 (x = 0) and MnCo 2 O 4 (x = 1) were prepared in powder form at low temperature by thermal decomposition of nitrates in air. The synthesis was conducted at 150ºC. The oxides obtained were characterized by different techniques such as X-ray diffraction (XRD), scanning electron microscopy (SEM), surface area determination using the Brunauer-Emmett-Teller (BET) method, thermogravimetric analyses (TGA) and oxidation power (OP). XRD analysis reveals that the oxides crystallize in a cubic spinel-type structure with a unit cell parameter (a o) that increases as cobalt is replaced by manganese. The MnCo 2 O 4 showed 70 m 2 g-1 and 13 nm of specific surface area and crystallite size respectively. The crystallite was bigger (20nm) when cobalt-manganese oxide is prepared as a thin film. Both compounds exhibited nanometric size. The cationic distributions proposed for both oxides on the basis of the physicochemical characterization results showed an excellent agreement with those obtained from the XRD data refinement performed using the Rietveld method.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.